Construction: Circular polyester weave extruded internally and externally with NBR-PVC.
Hose shall be made from 100% high tenacity synthetic yarn circular woven and completely, protected and locked-in by tough highly resistant synthetic nitrile rubber, forming a single homogenous construction without the use of glues or adhesives of any type.
Lining Properties:
a. Ultimate Tensile Strength:
Tensile strength of the lining and cover shall not be less than 1500 psi (10,500 kpa ).
b. Ultimate Elongation:
400% minimum.
c. Accelerated Aging Test
The tensile strength and ultimate elongation of the vulcanized rubber compound which has been subjected to the action of oxygen at a pressure of 300 psi +/- 10 psi , (2100kpa +/- 70kpa) and temperature of 70 degrees centigrade +/-1 degree centigrade (158 F +/- 18 F ) for a period of 96 hours shall be , greater than 60% of the original properties stated.
Color:Black ribbed
Temperature range:From -20 C deg to 80 C deg (-4 F deg to 176 F deg)
Elongation at WP:<1.5%
Expansion at WP:<6%
Abrasion:6000 DIN cycles
Standard Length: 660ft
Applications:
• Washdown
• Drainage pumps
• Water Discharge
• Drainage
• Irrigation installations
• Pumping of sludge and liquid fertilizers
• Temporary installations (by-passes)
*Not recommended or approved for fire fighting or frac water transferring.
Recommended for Industrial Water Discharge Solution.
Comparable to
Oroflex 10 of Tipsa, Superflow of Key, etc.
| NOMINAL | THICKNESS | WEIGHT | WORKING PRESSURE | ||
| inches | inches | mm | lbs/ft | grams/m | psi/bar |
| 1 1/2 | 0.08 | 2.2 | 0.21 | 320 | 150 /10 |
| 2 | 0.08 | 2.2 | 0.32 | 470 | 150 /10 |
| 2 1/2 | 0.08 | 2.2 | 0.44 | 650 | 150 /10 |
| 3 | 0.1 | 2.5 | 0.48 | 720 | 150 /10 |
| 4 | 0.1 | 2.6 | 0.66 | 980 | 150 /10 |
| 5 | 0.12 | 3 | 1.01 | 1500 | 150 /10 |
| 6 | 0.12 | 3.2 | 1.14 | 1700 | 150 /10 |
| 8 | 0.12 | 3.2 | 1.54 | 2300 | 150 /10 |
| 10 | 0.14 | 3.5 | 1.94 | 2900 | 150 /10 |
| 12 | 0.2 | 4 | 2.21 | 3300 | 150 /10 |